Damage accumulation of graded steel



Details zur Publikation
Autor(inn)en:
Besel, M.; Zeismann, F.; Mannel, J.; Brückner-Foit, A.
Publikationsjahr:
2010
Zeitschrift:
Engineering Failure Analysis
Seitenbereich:
633-640
Jahrgang/Band:
17
Erste Seite:
633
Letzte Seite:
640
ISSN:
1350-6307

Zusammenfassung, Abstract
The damage evolution of graded steel is studied. Specimens are taken out of a flange shaft having a graded microstructure resulting from thermo-mechanical forming process. Fatigue experiments are performed for the base material with a ferritic-pearlitic microstructure as well as for the nearly fully martensitic microstructure which is found in the outer area of the flange. The surface damage evolution during fatigue loading is investigated using a long-distance microscope. The base material shows very complex damage accumulation process with a high density of microcracks whereas the martensitic specimens exhibit no pronounced surface damage evolution prior to failure. (C) 2008 Elsevier Ltd. All rights reserved.


Autor(inn)en / Herausgeber(innen)

Zuletzt aktualisiert 2019-01-11 um 16:04